近期,我院教师张刘挺、研究生孙泽、蔡泽亮、颜年华、陆雄等的研究成果“Enhanced hydrogen storage properties of MgH2 by the synergetic catalysis of Zr0.4Ti0.6Co nanosheets and carbon nanotubes”在《Applied Surface Science》(IF=5.155)上发表。

发布时间:2020-01-03浏览次数:543

论文简介如下:

Transition metal nanoparticles have shown great catalytic effecton MgH2, yet excellent cyclic stability can be attached due to the addition of carbon nanotubes. In this paper, MgH2+10 wt% Zr0.4Ti0.6Co /5 wt% Carbon nanotubes (CNTs) composite is designed to investigate the synergistic modification of Zr0.4Ti0.6Co nanosheets and carbon nanotubes on the hydrogen storage performance of MgH2. Compared with pure MgH2,the initial hydrogen release temperature of MgH2+10 wt% Zr0.4Ti0.6Co /5 wt% CNTs composite decreases to 180 °C and the composite can quickly release 90% H2 within 10 min at 300 °C. In addition, the completely dehydrogenated sample can absorb 3.51 wt % H2 within 20 min under3 Mpahydrogen pressure at 125 °C.Ulteriorly, the activation energy valuesof dehydrogenation and rehydrogenation of MgH2 decrease to 70.5±7.8 kJ/mol and 35.8±3.8 kJ/mol on account of the presence of 10wt% Zr0.4Ti0.6Co/5wt% CNTs, which reasonably explains the remarkable reduction of the temperature for hydrogen sorption. Furthermore, the MgH2+10 wt% Zr0.4Ti0.6Co /5 wt% CNTs composite shows excellent cycling performance, indicative of potential application in practical hydrogen storage in the nearest future.

全文下载:https://xs.xiayige.org/scholar_url?url=https%3A%2F%2Fwww.sciencedirect.com%2Fscience%2Farticle%2Fpii%2FS0169433219332817&hl=zh-CN&sa=T&ct=res&cd=0&d=1444386092620608097&ei=7lAEXqKIMpC-yQTqr5TYCg&scisig=AAGBfm30pANfvcYd3Kbh2SNytYU1hfGupw&nossl=1&ws=1889x911&at=Enhanced%20hydrogen%20storage%20properties%20of%20MgH2%20by%20the%20synergetic%20catalysis%20of%20Zr0.%204Ti0.%206Co%20nanosheets%20and%20carbon%20nanotubes